Лінейны поліэтылен нізкай шчыльнасці, мадыфікаваны малеінавым ангідрыдам, сумяшчальны сплаў з нізкім дымам, безгалагенны антыпірэн W1L

Асноўная формула вогнеахоўнага кабельнага матэрыялу з нізкім утрыманнем дыму без галагенаў

It can be seen from Figure 1 that the addition of 5% W1L increases the tensile strength of the low-smoke halogen-free flame retardant cable compound system by 90% and the elongation at break by 135%.

Паляпшэнне ўласцівасцей пры расцяжэнні вогнеахоўнага кабельнага матэрыялу з нізкім утрыманнем дыму без галагенаў

Application effect of W1L in talc (20%) filled LLDPE system

Effect of W1L on Tensile Properties of Talc (20%) Filled LLDPE System

It can be seen from the figure that in the LLDPE system filled with talc (20%), adding 3% W1L can greatly improve the tensile strength, flexural strength and notched impact strength of the material system.

Прапанаваная доза:Доза (5-25%) можа быць адпаведна павялічана або зменшана ў адпаведнасці з патрабаваннямі да трываласці і з улікам кошту. 3-10% павінны быць прыняты для ўзмацнення і ўмацавання PA6/PA66, у той час як 5% павінны быць прыняты для сумясцільнік нейлону і сплаву поліпрапілена/поліэтылену.

Ўпакоўка, захоўванне і транспарціроўка:Крафт-мяшок 20 кг з унутраным поліэтыленавым пакетам. Гэты прадукт павінен разглядацца як бяспечны тавар і захоўвацца або транспартавацца ў сухіх умовах, пазбягаючы сонечнага святла і дажджу.

W1L is a method of chemical reaction to connect maleic anhydride molecules on the linear low-density polyethylene molecular chain, so that the polyethylene end has the re-reactivity and strong polarity of maleic anhydride polar molecules, so it can improve polyolefin. The interface affinity between the substrate and inorganic substances such as metal powder, glass fiber, wood powder, mineral powder, starch, etc., so as to enhance the strength of the composite material, and is often used as a compatibilizer for polyolefin materials. When this product is used in low-smoke halogen-free flame retardant cable compound, it can improve the compatibility and adhesion between polyolefin matrix and inorganic flame retardant interface. Improve the dispersibility and compatibility of magnesium hydroxide and aluminum hydroxide, so as to maximize the flame retardancy of cable materials, reduce smoke index, smoke generation, calorific value and carbon monoxide generation, increase oxygen index, improve dripping Falling properties, etc., improve the mechanical properties of materials. This product can also be used as a surface improver for extruded sheet or extruded sheet, which can effectively improve the surface flatness of sheet or sheet, and eliminate unevenness and pitting on the surface of the material.